Alumina microcystal wear resisting lining are made with high tech-forula materials under 1500℃ temperature firing in kiln. It has high compression strength, better wear resistance and high hardness.
It can be used in different industry for wear resistance grinding equipment such as oil, mine, steel and electricity industry to protect damage of the machine from impact of the raw material, erosion from chemical substances and the heat shock, reduce the abrasion to the machines and equipment, can save the maintain cost, extend the life of the machines.
Technical data:
Item | Ceramic alumina tiles |
Al2O3 content | ≥92% |
Fe2O3 content | ≤0.01% |
Density | ≥3.60g/cm3 |
Abrasion | ≤0.01% |
Hardness | 9mohs |
HS Code | 69091200.00 |
Size | Can be customized. |
Product feature:
High hardness
Rockwell hardness is HRA80-90, just less than diamond but much higher than wear-resistant steel and stainless steel.
Excellent abrasive resistance
266 times more than Mn-steel for abrasive resistance, 171.5 times more than high Cr-steel.
Light weight
The density is 3.6g/cm3 which just half of the steel, it can reduce the load of the machine.
Firmly bonded with good heat resistance
Alumina lining usually installed with heat-resisting glue for machines. Can work under 350℃ long time without damage.
Product introduction & Application:
Alumina microcystal wear resisting lining are made with high tech-forula materials under 1500℃ temperature firing in kiln. It has high compression strength, better wear resistance and high hardness.
It can be used in different industry for wear resistance grinding equipment such as oil, mine, steel and electricity industry to protect damage of the machine from impact of the raw material, erosion from chemical substances and the heat shock, reduce the abrasion to the machines and equipment, can save the maintain cost, extend the life of the machines.
Technical data:
Item | Ceramic alumina tiles |
Al2O3 content | ≥92% |
Fe2O3 content | ≤0.01% |
Density | ≥3.60g/cm3 |
Abrasion | ≤0.01% |
Hardness | 9mohs |
HS Code | 69091200.00 |
Size | Can be customized. |
Product feature:
High hardness
Rockwell hardness is HRA80-90, just less than diamond but much higher than wear-resistant steel and stainless steel.
Excellent abrasive resistance
266 times more than Mn-steel for abrasive resistance, 171.5 times more than high Cr-steel.
Light weight
The density is 3.6g/cm3 which just half of the steel, it can reduce the load of the machine.
Firmly bonded with good heat resistance
Alumina lining usually installed with heat-resisting glue for machines. Can work under 350℃ long time without damage.