Brief introduction & application:
Ready to press powder/Granulation powder is widely used in grinding materials, Refractory, Water purification filter, Fertilizer, Ceramic raw materials & High Grade Fine ceramic raw materials, etc. Due to their high performance and precision, fine ceramics are now used in a variety of industrial applications, especially in the electronics industry.
Application:
↙ ↘
Technical data:
Ceramic material | Alumina | |||||||
General composition | Al2O3 | Al2O3 | Al2O3 | Al2O3 | Al2O3 | Al2O3 | Al2O3 | Al2O3 |
Classification name | AKP-20M | MS-3N12 | MG995C | LS- 711C-W | LS- 771C-P | LS-711CB-W | BA-95 | A-96A |
Color | White | White | Ivory | Ivory | Ivory | Ivory | Black | White |
Content % | 99.99 | 99.9 | 99.5 | 99.5 | 99.5 | 99.5 | 95 | 96 |
Property | ||||||||
Bulk density g/cm3 | 1.2 | 1.1 | 1.1 | 1.1 | 1.1 | 1.1 | 1.2 | 1.1 |
Green density g/cm3 | 2.4 | 2.4 | 2.4 | 2.3 | 2.4 | 2.4 | 2.3 | 2.3 |
Fired density g/cm3 | 3.9 | 3.9 | 3.9 | 3.9 | 3.9 | 3.9 | 3.9 | 3.6 |
BET Specific Surface area m2/g | 4.6 | — | 3.8 | 5.9 | 5.9 | 5.9 | — | — |
Fineness D50=μm | 0.5 | 0.5 | 0.9 | 0.7 | 0.7 | 0.7 | 0.7 | 3.0 |
Water absorption % | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 |
Flexural strength Mpa | 450 | 400 | 450 | 450 | 450 | 500 | 250 | 420 |
Shrinking percentage % | 16.0 | 16.4 | 16.5 | 17.2 | 16.6 | 16.5 | 17.7 | 15.6 |
Ignition loss % | 5.0 | 5.1 | 5.5 | 5.1 | 6.3 | 5.1 | 5.8 | 5.2 |
Notes | 1550℃ 3HR | 1550℃ 3HR | 1550℃ 3HR | 1550℃ 3HR | 1550℃ 3HR | 1550℃ 3HR | 1300℃ 3HR | 1550℃ 3HR |
Ceramic material | Alumina | Mulite | Compsite material | Refractory | ||||
General composition | Al2O3 | Al2O3 | Al2O3 | 3(Al2O3) · 2(SiO2) | Al2O3 · SiO2 | Al2O3 & ZrO2 | Fused Al2O3 | Fused Al2O3 |
Classification name | AL-9640 | LAL-964A | A-801 | A-706 | A-55L | AZ-30 | WAL-99 | FZC |
Color | White | White | White | White | White | White | White | Yellow |
Content % | 96 | 96 | 80 | 70 | 99 | 99 | ||
Property | ||||||||
Bulk density g/cm3 | 1.1 | 1.1 | 1.1 | 1.0 | 0.9 | 1.1 | 1.2 | 1.3 |
Green density g/cm3 | 2.2 | 2.2 | 2.5 | 2.2 | ||||
Fired density g/cm3 | 3.8 | 3.7 | ||||||
BET Specific Surface area m2/g | — | — | ||||||
Fineness D50=μm | 1.1 | 0.7 | ||||||
Water absorption % | 0 | 0 | 0 | 0 | 0 | 0 | 3.6 | 4.1 |
Flexural strength Mpa | 250 | 350 | 280 | 220 | 140 | 560 | 140 | 11 |
Shrinking percentage % | 18.6 | 18.6 | 16.5 | 14.9 | 15.6 | 17.2 | 11.7 | 4.1 |
Ignition loss % | 7.9 | 7.3 | 5.5 | 8.7 | 8.3 | 6.4 | 7.4 | 6.3 |
Notes | 1550℃ 3HR | 1400℃ 3HR | 1350℃ 3HR | 1300℃ 3HR | 1550℃ 3HR | 1500℃ 3HR | 1600℃ 3HR | 1600℃ 3HR |
Support adjusted according to customer's requirements! | ||||||||
Product feature:
High quality, the precision of granulation is high and the purity is controlled;
High Hardness;
High Compression Strength;
Abrasion/Wear-Resistance;
Chemical Inertness;
High Degree of Refractoriness;
Superior Insulating Properties;
Resistance to Thermal Shock;
High Melting Point.
Advantage:
Produced by Marumi Toryo Co.,Ltd (Japan)
Agent: Dalian Gaoteng Company
Can be customized according to customer requirements.
High purity alumina granule (mold, CIP) is our main product. We also deal with zirconia, mullite, cordierite, such oxide granule raw materials. Granulation production can be adjusted as any requirements and providing stable products in any quantity.
Professional technical services & support
Origin of Japan, quality assurance
Brief introduction & application:
Ready to press powder/Granulation powder is widely used in grinding materials, Refractory, Water purification filter, Fertilizer, Ceramic raw materials & High Grade Fine ceramic raw materials, etc. Due to their high performance and precision, fine ceramics are now used in a variety of industrial applications, especially in the electronics industry.
Application:
↙ ↘
Technical data:
Ceramic material | Alumina | |||||||
General composition | Al2O3 | Al2O3 | Al2O3 | Al2O3 | Al2O3 | Al2O3 | Al2O3 | Al2O3 |
Classification name | AKP-20M | MS-3N12 | MG995C | LS- 711C-W | LS- 771C-P | LS-711CB-W | BA-95 | A-96A |
Color | White | White | Ivory | Ivory | Ivory | Ivory | Black | White |
Content % | 99.99 | 99.9 | 99.5 | 99.5 | 99.5 | 99.5 | 95 | 96 |
Property | ||||||||
Bulk density g/cm3 | 1.2 | 1.1 | 1.1 | 1.1 | 1.1 | 1.1 | 1.2 | 1.1 |
Green density g/cm3 | 2.4 | 2.4 | 2.4 | 2.3 | 2.4 | 2.4 | 2.3 | 2.3 |
Fired density g/cm3 | 3.9 | 3.9 | 3.9 | 3.9 | 3.9 | 3.9 | 3.9 | 3.6 |
BET Specific Surface area m2/g | 4.6 | — | 3.8 | 5.9 | 5.9 | 5.9 | — | — |
Fineness D50=μm | 0.5 | 0.5 | 0.9 | 0.7 | 0.7 | 0.7 | 0.7 | 3.0 |
Water absorption % | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 |
Flexural strength Mpa | 450 | 400 | 450 | 450 | 450 | 500 | 250 | 420 |
Shrinking percentage % | 16.0 | 16.4 | 16.5 | 17.2 | 16.6 | 16.5 | 17.7 | 15.6 |
Ignition loss % | 5.0 | 5.1 | 5.5 | 5.1 | 6.3 | 5.1 | 5.8 | 5.2 |
Notes | 1550℃ 3HR | 1550℃ 3HR | 1550℃ 3HR | 1550℃ 3HR | 1550℃ 3HR | 1550℃ 3HR | 1300℃ 3HR | 1550℃ 3HR |
Ceramic material | Alumina | Mulite | Compsite material | Refractory | ||||
General composition | Al2O3 | Al2O3 | Al2O3 | 3(Al2O3) · 2(SiO2) | Al2O3 · SiO2 | Al2O3 & ZrO2 | Fused Al2O3 | Fused Al2O3 |
Classification name | AL-9640 | LAL-964A | A-801 | A-706 | A-55L | AZ-30 | WAL-99 | FZC |
Color | White | White | White | White | White | White | White | Yellow |
Content % | 96 | 96 | 80 | 70 | 99 | 99 | ||
Property | ||||||||
Bulk density g/cm3 | 1.1 | 1.1 | 1.1 | 1.0 | 0.9 | 1.1 | 1.2 | 1.3 |
Green density g/cm3 | 2.2 | 2.2 | 2.5 | 2.2 | ||||
Fired density g/cm3 | 3.8 | 3.7 | ||||||
BET Specific Surface area m2/g | — | — | ||||||
Fineness D50=μm | 1.1 | 0.7 | ||||||
Water absorption % | 0 | 0 | 0 | 0 | 0 | 0 | 3.6 | 4.1 |
Flexural strength Mpa | 250 | 350 | 280 | 220 | 140 | 560 | 140 | 11 |
Shrinking percentage % | 18.6 | 18.6 | 16.5 | 14.9 | 15.6 | 17.2 | 11.7 | 4.1 |
Ignition loss % | 7.9 | 7.3 | 5.5 | 8.7 | 8.3 | 6.4 | 7.4 | 6.3 |
Notes | 1550℃ 3HR | 1400℃ 3HR | 1350℃ 3HR | 1300℃ 3HR | 1550℃ 3HR | 1500℃ 3HR | 1600℃ 3HR | 1600℃ 3HR |
Support adjusted according to customer's requirements! | ||||||||
Product feature:
High quality, the precision of granulation is high and the purity is controlled;
High Hardness;
High Compression Strength;
Abrasion/Wear-Resistance;
Chemical Inertness;
High Degree of Refractoriness;
Superior Insulating Properties;
Resistance to Thermal Shock;
High Melting Point.
Advantage:
Produced by Marumi Toryo Co.,Ltd (Japan)
Agent: Dalian Gaoteng Company
Can be customized according to customer requirements.
High purity alumina granule (mold, CIP) is our main product. We also deal with zirconia, mullite, cordierite, such oxide granule raw materials. Granulation production can be adjusted as any requirements and providing stable products in any quantity.
Professional technical services & support
Origin of Japan, quality assurance