Introduction:
| Name | Chemical contents | Wear loss | Density | Processing technic |
| TZP Yttrium Stabilized Zirconia Beads | ZrO2: 94.8% Y2O3: 5.2% | 3ppm/h | 6g/cm3 | Sintering |
| Avaliable size: 0.05-0.1mm 0.1-0.2mm 0.2-0.3mm 0.3-0.4mm 0.4-0.6mm 0.6-0.8mm 0.8-1.0mm 1.0-1.2mm 1.2-1.4mm 1.4-1.6mm 1.6-1.8mm 1.8-2.0mm 2.0-2.2mm 2.2-2.4mm 2.4-2.6mm 2.6-2.8mm 2.8-3.0mm 3.0-3.5mm 3.5-4.0mm 4.0-4.5mm 4.5-5.0mm 5.0-5.5mm 5.5-6.0mm 6.0-6.5mm 6.5-7.0mm Other size can be customized. | ||||
| Surface: White color, smooth surface, pearly luster | ||||
Made of micron and sub-nanometer raw materials and advanced technology, all technical indicators and performance have reached the international advanced level.
1. The sphere has good roundness, smooth surface and pearl-like luster.
2. It has excellent toughness, impact resistance, and will not break during high-speed operation.
3. The wear resistance of yttrium-stabilized zirconia beads is 30-50 times that of glass beads
4. Yttrium-stabilized zirconia beads have a higher density than other grinding beads and have extremely high grinding efficiency, which can increase the solid content of the material or increase the material flow rate.
5. Corrosion-resistant, wear-resistant, essential for grinding and dispersing nano-scale materials, best matched with pin-type and turbine-type sand mills
6. PPM-level abrasion prevents cross-contamination between beads and base materials, and does not contain heavy metals, effectively ensuring the purity of pharmaceutical, chemical and other materials during the grinding process.
Applicable equipment:
rod pin horizontal sand mill, turbine horizontal sand mill, irregular dispersed disc sand mill, ring sand mill, centrifugal sand mill, basket sand mill, nano sand mill and other equipment.
Packing:
The zirconia balls are dispatched in strong plastic barrel, and for better conservation, also with plastic bag inside.
Normally the standard package is 25KG/barel, 1-1.5tons/pallet.
Introduction:
| Name | Chemical contents | Wear loss | Density | Processing technic |
| TZP Yttrium Stabilized Zirconia Beads | ZrO2: 94.8% Y2O3: 5.2% | 3ppm/h | 6g/cm3 | Sintering |
| Avaliable size: 0.05-0.1mm 0.1-0.2mm 0.2-0.3mm 0.3-0.4mm 0.4-0.6mm 0.6-0.8mm 0.8-1.0mm 1.0-1.2mm 1.2-1.4mm 1.4-1.6mm 1.6-1.8mm 1.8-2.0mm 2.0-2.2mm 2.2-2.4mm 2.4-2.6mm 2.6-2.8mm 2.8-3.0mm 3.0-3.5mm 3.5-4.0mm 4.0-4.5mm 4.5-5.0mm 5.0-5.5mm 5.5-6.0mm 6.0-6.5mm 6.5-7.0mm Other size can be customized. | ||||
| Surface: White color, smooth surface, pearly luster | ||||
Made of micron and sub-nanometer raw materials and advanced technology, all technical indicators and performance have reached the international advanced level.
1. The sphere has good roundness, smooth surface and pearl-like luster.
2. It has excellent toughness, impact resistance, and will not break during high-speed operation.
3. The wear resistance of yttrium-stabilized zirconia beads is 30-50 times that of glass beads
4. Yttrium-stabilized zirconia beads have a higher density than other grinding beads and have extremely high grinding efficiency, which can increase the solid content of the material or increase the material flow rate.
5. Corrosion-resistant, wear-resistant, essential for grinding and dispersing nano-scale materials, best matched with pin-type and turbine-type sand mills
6. PPM-level abrasion prevents cross-contamination between beads and base materials, and does not contain heavy metals, effectively ensuring the purity of pharmaceutical, chemical and other materials during the grinding process.
Applicable equipment:
rod pin horizontal sand mill, turbine horizontal sand mill, irregular dispersed disc sand mill, ring sand mill, centrifugal sand mill, basket sand mill, nano sand mill and other equipment.
Packing:
The zirconia balls are dispatched in strong plastic barrel, and for better conservation, also with plastic bag inside.
Normally the standard package is 25KG/barel, 1-1.5tons/pallet.